South America Area Suitable Silver Sandblasting Anodized Aluminum Extrusion Profiles
Introduction of Extrusion:
1: Extrusion principle of aluminum profile
Extrusion is a kind of plastic processing method that applies external force to the metal blank placed in the container (extrusion cylinder) to make it flow out of the specific die hole to obtain the required cross-section shape and size.
2: Structure of aluminum extrusion press
The extruder is composed of base, front column frame, tension column, extrusion cylinder and hydraulic system under electrical control. It is also equipped with die base, thimble, scale plate, sliding plate, etc.
3: Classification of aluminum extrusion methods
According to the type of metal in the extrusion cylinder, stress-strain state, extrusion direction, lubrication state, extrusion temperature, extrusion speed, type or structure of tool and die, shape or number of blank, shape or number of products, it can be divided into forward extrusion method, reverse extrusion method (including plane deformation extrusion, axisymmetric deformation extrusion, general three-dimensional deformation extrusion) and lateral extrusion method, Glass lubrication extrusion, hydrostatic extrusion, continuous extrusion and so on.
4: Forward hot deformation aluminum extrusion
The vast majority of hot deformation aluminum production enterprises adopt the forward hot deformation extrusion method to obtain the aluminum with the required cross-section shape through specific dies (flat die, cone die, split die). This is the only aluminum production method adopted by jinhaochun aluminum so far!
The forward extrusion process is simple, the equipment requirements are not high, the metal deformation ability is high, the production range is wide, the aluminum performance is controllable, the production flexibility is large, and the tooling is easy to maintain and correct.
Product Details:
| Description | South America Area Suitable Silver Sandblasting Anodized Aluminum Extrusion Profiles 6063 T5 Alloy |
| Material Thickness(t) | t=0.8-2.0 mm |
| Materiral | Aluminum Alloy 6063 |
| Annealing Treatment | T3-T8 |
| Color | Champagne, Silver White ,Bronze, Grey, Black, (RAL series)etc. |
| Surface Treatment | electrophoresis, anodized, wood grain, polished and etc |
| Shape | Break Bridge,T Shape,Square, Round, Flat, Oval, and according to customer's drawing. |
| Length | Normal length=6m or in customer's order |
| Usage | Building, Production Line, Decoration, Industrial, Transportation, Door and window, etc. |
| Package | 1. Pearl cotton foam for each profile; 2. Wrap with shrink film exterior; 3. Packed according to customer request. |
| Advantages/Features | Providing colorful products with various mechanical performances to adapt all kinds of architectural styles |
Introduction of Electrophoresis:
Aluminum or aluminum alloy products are used as anodes in electrolyte solution, and the process of forming aluminum oxide film on the surface of the aluminum and aluminum alloy is called anodic oxidation treatment of aluminum and aluminum alloy. After anodization, the surface of aluminum can produce several microns - hundreds of microns of oxide film. Compared with the natural oxide film of aluminum alloy, its corrosion resistance, wear resistance and decoration have been obviously improved and improved.
- The aluminum oxide film is a porous membrane. Whether it is coloured or not, it must be closed before being put into use, so as to improve its corrosion resistance and weatherability. There are three kinds of treatment methods, namely, high temperature hydration reaction closed, inorganic salt closure and organic matter closure.
(1) High temperature water sealing.
This method utilizes the hydration reaction of aluminum oxide film and water to turn the amorphous membrane into a hydrated crystalline membrane.
The hydration reaction can be carried out at both normal and high temperatures, but at high temperatures, especially at the boiling point, the hydrated crystalline membrane is a very stable and irreversible crystalline film. Therefore, the most commonly used aluminum oxide film is treated by boiling water or steam treatment.
(2) Sealing of inorganic salts.
Inorganic salt method can improve the fastness of organic coloring dyes, so it is often used in chemical coloring.
(3) Organic sealing method.
This is the soaking, soaking or coating of the aluminum oxide film. Because of the high cost and the increase of the process flow, it is not easy to use, more or more of the two kinds of methods mentioned above, and the first kind of high temperature hydration is the mainstream.
| Implement National Standard | GB/5237.2-2008 |
| Ingot State | Nonferrous mental industrial standard YS67-93 |
| Chemical Of Oxide Film | GB/T3190-96 |
| Class Of Oxide Film | AA10 , AA15 ,AA20 |
| Surface Type | Matte ,Flat |
| Colors | Silver , White ,Bronze , Champagne |
| Advantage/Features | Corrosion-Resistant , Durable , Shining And Decorative |
Photos:
Please tell us the information below, and we will give the best suggestion to you !
1. Where you intend to use the aluminium profiles?
2. If you have the estrusion drawing, send us and we develop the correspondence mold.
3. Which color you want or tell us the architectural style you like.
4. Purchase quantity. It will convenient us to give you the best price.